The model of recombination process in TlBr
2002
The time-resolved luminescence was used as a tool in the study of recombination process in several undoped TlBr crystals. The spectra and decay kinetics observed under electron beam excitation were investigated. Observation of several luminescence bands with different decay rates shows that more than one recombination center is involved and the recombination process is quite complicated. The band at ∼2.5 eV is dominant under 10 ns excitation pulse (electron beam or nitrogen laser pulses). The results of short-lived absorption and luminescence are used for analysis of possible mechanisms of recombination processes in TlBr.
Luminescence of ferroelectric crystals: LiNbO3and KNbO3
2000
Abstract The thermostimulated luminescence and time-resolved luminescence of LiNbO3 (congruent, stoichiometric, Eu−, Mn−, or Cr−doped) and KNbO3 crystals (undoped, Fe−, or Mn− doped) excited by X-ray, pulsed nitrogen laser or pulsed electron beam were studied. The luminescence decay times of niobium-oxygen groups (regular or perturbed by defect or impurity) were obtained. It is shown that the energy transfer from bulk to the activator in LiNbO3 is not effective during the electron-hole recombination process.
Luminescence spectra and decay kinetics in ZnWO4 and CdWO4 crystals
2004
The luminescence spectra and luminescence decay kinetics in ZnWO4 (nominal pure and doped with Fe and Mo) under pulsed electron beam and pulsed nitrogen laser excitation have been investigated. It is suggested that the two-stage intrinsic luminescence decay observed under ionizing radiation excitation in ZnWO4 and CdWO4 was due to two different self-trapped exciton (STE) configurations in these crystals. The role of Fe and Mo impurities for scintillation efficiency in ZnWO4 and CdWO4 has been discussed. (© 2004 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)
Luminescence of GeO2 glass, rutile-like and α-quartz-like crystals
2006
Abstract The luminescence of GeO 2 rutile-like crystals was studied. Crystals were grown from a melt of germanium dioxide and sodium bicarbonate mixture. Luminescence of the crystal was compared with that of sodium germanate glasses produced in reduced and oxidized conditions. A luminescence band at 2.3 eV was observed under N 2 laser (337 nm). At higher excitation photon energies and X-ray excitation an additional band at 3 eV appears in luminescence. The band at 2.3 eV possesses intra-center decay time constant about 100 μs at 290 K and about 200 μs at low temperature. Analogous luminescence was obtained in reduced sodium germanate glasses. No luminescence was observed in oxidized glasses…
Time-resolved spectroscopy of ZnWO4
2001
The luminescence spectra of ZnWO 4 excited by a pulsed electron beam, pulsed nitrogen laser and X-ray are studied. The luminescence decay kinetics are compared with transient absorption relaxation kinetics. Broad band transient absorption spectra are observed and it is shown that the slow decay component (∼14 μs at RT) of the transient absorption matches well with the luminescence decay therefore this absorption is due to the excited state absorption of the luminescence center.